Replacing Fender "knife edge" pivots.
Posted: Tue Nov 27, 2018 11:37 am
I have stripped down my Fender Artist D-10 for maintenance and find one pivot blade badly worn in three places, the other worn a bit less. For those not familiar with the thing I'll explain. And, by the way, these Fenders are the ones with the ShoBud undercarriage. I'm in UK.
The fingers do not pivot on a rod. The fulcrum is a knife-edge and the fingers have a ">" shape that sits on the knife-edge. This results in almost no friction. The "blade" is some alloy or aluminium (too light and too worn to be steel) and 3.5in x 1in x 1/10th in thick. I don't think the thickness is critical; 2.5mm or even 3mm (with the edge filed a bit sharper at the edge) would do.
Does anyone have any ideas what material I need to search for? I'm not familiar with aluminium grades. I even considered 3mm brass
Any thoughts would be helpful, from a PSG tech. or a metal workers angle.
One other thought occurred to me, I wondered if the Fender 800 or 2000 used the same knife - it would be logical that an existing part would be used in the new model.
The fingers do not pivot on a rod. The fulcrum is a knife-edge and the fingers have a ">" shape that sits on the knife-edge. This results in almost no friction. The "blade" is some alloy or aluminium (too light and too worn to be steel) and 3.5in x 1in x 1/10th in thick. I don't think the thickness is critical; 2.5mm or even 3mm (with the edge filed a bit sharper at the edge) would do.
Does anyone have any ideas what material I need to search for? I'm not familiar with aluminium grades. I even considered 3mm brass
Any thoughts would be helpful, from a PSG tech. or a metal workers angle.
One other thought occurred to me, I wondered if the Fender 800 or 2000 used the same knife - it would be logical that an existing part would be used in the new model.